Quick Details
Place of Origin: China (Mainland) Brand Name: XINCHENG
Product name: High strength insulation FRP screw and nut Application: High Voltage
Surface Treatment: Smooth or process according to requirement Technique: Pultrusion and machined
Dimensions: 2mm-100mm and Customizable Material: fiberglass, epoxy resin
Raw material:: polyester resin, epoxy resin, vinylest Model Number: M3-M64 and Customizable
Type: Hexagon head, Round head, Square or Customized Standard: IEC61109
Bending strength: ≥960 Mpa Bending strength at heating conditions: ≥350
Torsion strength: ≥800 Mpa Length: Customized Length
Certificate: ISO9001 Color: light green or Customized Colors
Density:: 1.2-2.0 g/cm3 Tensile Strength: 10.4Mpa
Temperature: 120ºC-180ºC The insulation grade: H class
Rated Voltage: 25KV Usage: Insulation Protection
Size: Customized Size Certification: ISO9001:2008,ROHS, SGS
Our FRP bolts made of E-glass fiber and epoxy resin, depends on different requirements, carbon fiber and vinyl ester resin also be available.
1.Use unique fiberglass -oriented method, it has excellent high strength, high durable and high corrosion-resist.
2.It's surface without magnetism, no impurities be attached.
3.Light weight, it's only 1/4 of carbon steel.
4.It can works well under the condition with different temperature.
5.The resin content of outer surface is higher (>95%), it has excellent corrosion resist property.
6.It's has good electrical insulation and heat insulation.
FRP fasteners like FRP bolts, FRP studs, FRP nuts, FRP threaded rods, FRP bolts, etc. are being used for joining of Channels, Flats, etc. In chemical plants, fertilizer plants, off shore project, cooling towers, FRP fasteners are being used in joints instead of metallic or PVC fasteners. They are used wherein metallic fasteners are prohibited. These products are available in different dimensions as per the needs and specifications of different clients in various industries.
Standard sizes available :
Stud: M 6,8,10,12,16,20,24,25 mm
Nut: M 6,8,10,12,16,20 mm
Threaded Rod: M 6,8,10,12,16,20,25 mm
Also the above can be customized.
Epoxy laminated glass-fiber specification
Application
Fiberglass / FRP/ GRP bolts and nuts using high-strength fiberglass impregnated epoxy resin matrix at high temperature pultrusion. After CNC process, grinding, special surface treatment made of insulated bolts and nuts.
Bolts and nuts have a special treatment by the surface, so that the bolts and nuts have good flexibility, excellent wear resistance, excellent resistance to voltage performance. Products applicable to transformers, reactors, special high-voltage converter valve, and other special high-voltage electrical appliances.
Our product is made of fiberglass and epoxy resin mixed continuous pultrusion, which makes the product resistance to mechanical stress and mechanical tension are very good, the tensile strength of 1500MPa, far more than 45 steel casting tensile strength 570Mpa indicators. Electrical performance, voltage level for the 10kV - 1000kV voltage range. Corrosion resistance, high bending strength, not easy to bend, easy to use and so on.
Products allow long-term working temperature of 170-210 ºC , product maximum short-circuit working temperature of 260 ºC (time is less than 5 seconds).
Products choose Germany release agent, so as to ensure that the surface of the product is very smooth without color difference, no glitches, no scratches.
The heat-resistant grade and the insulation grade of the product all reach H grade.
In addition to the above products, we also provide the following products.
EPGC201,EPGC202 board are from electrical alkali-free glass cloth with epoxy resin Baptist,formed by hot pressing,Products with high mechanical properties and electrical performance.
EPGC201 epoxy glass cloth laminate applied to B-class motors.electrical equipment for insulation of structural parts.
EPGC202 epoxy glass cloth laminated sheets have flame-retardant requirements applicable to the B-class motors.electrical equipment for insulation of structural parts as other Purposes.
Product Description
EPGC203,EPGC204 plates are from 7628 glass cloth with epoxy resin Baptist,formed by hot pressing.Products with high mechanical properties.
EPGC203 epoxy glass cloth laminate applied to F-class motors,electrical equipment for insulation of structural parts.
EPGC204 epoxy glass cloth laminated sheets have flame-retardant requirements applicable to the F-class motors,electrical equipment for insulation of structural parts.
Technical parameters
Technical parameters
Technical parameters
Polymer composite insulation rod
Using glass fiber impregnated in epoxy resin matrix pultrusion and after high temperature,The product has:light weight,machinery stable performance,excellent insulation performance,can override the 10KV-1000KV voltage range,Tensile properties of products is highlighted particularly,the tensile strength is 1360Mpa or above,significantly more than 45casting steel tensile strength 570Mpa index.Composite insulator composite dielectric properties provides reliable basis,The company production of the mandrel are:General mandrel,high temperature,acid,high temperature resistant mandrel mandrel acid-resistant core bar of four major series of products.
Technical parameters
Instruction:Dipped and stove to prep reg by electronic grade glass fiber cloth,epoxy,pyruvate,dicyandiamide.DMF and a small amount of chemical materials.
Character,
1.Glossy and smooth service.uniform thickness and without other impurities,
2.The specification and colors can be produced according to customers' requirement.
3.Time of g elation and percent of gel can controlled according to customers' requirement,
Width,1270mm,1260mm,1250mm,1100mm.
Thickness,7628/190g~20g 1506/150g~160g 2116/110g~130g
Color:pale green,pale yellow,anti-static and black.
Usage,Used to PCB CCL and various of isolation plates.
The company has processing center and advanced equipment.according to customer's pictures,drawings of samples of the design,production,processing services,for customers to find the best solution for the application of ,Products are mainly used in large motor,switch cabinets,electrical control cabinet, inverters,transformers and other fields.
Two benzene ether laminate,Have excellent mechanical properties,electrical properties and chemical corrosion resistance and radiation resistance,Applicable to H machinery,parts for electrical insulation in the results.
Melamine board.With high mechanical properties,electrical properties,and excellent flame retardancy and arc resistance,Suitable for electrical equipment for arc resistant insulation structural parts
Phenolic cotton cloth laminated rod:Has a certain mechanical,electrical properties,but in the use of transformer oil.used in electrical appliance insulation structural parts.
Laminate standard thickness:0.3mm-80mm
Laminate standard standard diameter:6mm-200mm
Remarks:Customer's special requirement on specifications could be negotiated by buyer and seller case by case
Glass Cloth Laminates Type:3240 series 3240,3240-1,3240-3,EPGC series EPGC 201,EPGC202,EPGC203,EPGC204,EPGC205,EPGC306,EPGC307,EPGC308;FR-4,FR-5,G-11,etc
Characteristics&Applications:With high mechanical strength,electrical properties and ,good moisture resistance properties,widely range of applications,for example:suitable for using as insulation structural parts in electric equipment,such as electric generators,motors,etc.
Phenolic Cotton Cloth Laminates Type:3025,3026,3027,3028;PFCC series PFCC201,PFCC202,PFCC203,FPCC204;C850 series C850.1,C850.2(CE),C850.3,C850.4(LE),etc
Characteristic&Applications:Widely range of applications in mechanical and electrical field,for example:suitable for using as insulation structural parts of machinery and electric equipment.such as electric generators,motors,switch board,e
Phenolic Paper Laminates Type:3020,3021 series 3021,302B,3021C,3021D;PFCP series of PFCP201,PFCP202,PFCP203,PFCP206,PFCP207,PFCP308,etc.
Characteristics&Applications:Widely range of applications,for examples,suitable for using as insulation structural parts of machinery and electric equipment,such as electric generators,motors,switch board,etc.
Molded Rod Type:phenolic cotton cloth rod 3721,3722,3723,3724,3725;epoxy glass cloth 3840,3841,etc.
Characteristics&Applications:Used in mechanical and electrical.
FAQ
1. Where are you located?
We are located in TIANJIN city, China, near to Beijing.
2. Do you accept small / sample order? And lead time?
Sample are available, lead time according factory production plan, uauslly 7-25 days.
3. How do you ship the goods?
We ship the goods by Sea, or by express, specific discussion.
4. Do you accept OEM or ODM order?
Yes, OEM and ODM order are welcome.
5. What payment do you accept?
L/C at sight, T/T, Western Union, etc.
Packaging & Delivery
Packaging Details
suitable packing for export. PP bag, Carton box, Pallet/ Or according customer requirement.
1.Inside packing: a plastic bag or woven belt
2.Outside packing: carton box and pallet.
3.According customer requirement.
Delivery Time: 3~7days
Please Contact Us
Miss: lydia
Mob: 86-13752439076 Fax: 86-22-60863016
http://chinainsulation.en.made-in-china.com
Place of Origin: China (Mainland) Brand Name: XINCHENG
Product name: High strength insulation FRP screw and nut Application: High Voltage
Surface Treatment: Smooth or process according to requirement Technique: Pultrusion and machined
Dimensions: 2mm-100mm and Customizable Material: fiberglass, epoxy resin
Raw material:: polyester resin, epoxy resin, vinylest Model Number: M3-M64 and Customizable
Type: Hexagon head, Round head, Square or Customized Standard: IEC61109
Bending strength: ≥960 Mpa Bending strength at heating conditions: ≥350
Torsion strength: ≥800 Mpa Length: Customized Length
Certificate: ISO9001 Color: light green or Customized Colors
Density:: 1.2-2.0 g/cm3 Tensile Strength: 10.4Mpa
Temperature: 120ºC-180ºC The insulation grade: H class
Rated Voltage: 25KV Usage: Insulation Protection
Size: Customized Size Certification: ISO9001:2008,ROHS, SGS
Our FRP bolts made of E-glass fiber and epoxy resin, depends on different requirements, carbon fiber and vinyl ester resin also be available.
1.Use unique fiberglass -oriented method, it has excellent high strength, high durable and high corrosion-resist.
2.It's surface without magnetism, no impurities be attached.
3.Light weight, it's only 1/4 of carbon steel.
4.It can works well under the condition with different temperature.
5.The resin content of outer surface is higher (>95%), it has excellent corrosion resist property.
6.It's has good electrical insulation and heat insulation.
FRP fasteners like FRP bolts, FRP studs, FRP nuts, FRP threaded rods, FRP bolts, etc. are being used for joining of Channels, Flats, etc. In chemical plants, fertilizer plants, off shore project, cooling towers, FRP fasteners are being used in joints instead of metallic or PVC fasteners. They are used wherein metallic fasteners are prohibited. These products are available in different dimensions as per the needs and specifications of different clients in various industries.
Standard sizes available :
Stud: M 6,8,10,12,16,20,24,25 mm
Nut: M 6,8,10,12,16,20 mm
Threaded Rod: M 6,8,10,12,16,20,25 mm
Also the above can be customized.
Epoxy laminated glass-fiber specification
| Heat Resistance | B | Standard | Q/DJ10-731-2000 |
| Density | ≥1.65g/cm3 | ||
| Hydroscopicity | < 0.60 MPA | ||
| Volume Resistively | Under normal | ≥1.0×1010 Ω.cm | |
| After immersion 24h | ≥1.0×108Ω.cm | ||
| Insulation Resistance | Under normal | ≥1.0×1010Ω | |
| After immersion 24h | ≥1.0×107Ω | ||
| Proof Voltage at perpendicular to lamination (transformer oil at 90± degree for 5 min) | MV/m | ≥8 | |
| Heat stability (150 degree ,/24 H ) | No crack or plump up | ||
Application
Fiberglass / FRP/ GRP bolts and nuts using high-strength fiberglass impregnated epoxy resin matrix at high temperature pultrusion. After CNC process, grinding, special surface treatment made of insulated bolts and nuts.
Bolts and nuts have a special treatment by the surface, so that the bolts and nuts have good flexibility, excellent wear resistance, excellent resistance to voltage performance. Products applicable to transformers, reactors, special high-voltage converter valve, and other special high-voltage electrical appliances.
| Very low temperature condition | refrigeration equipments, liquid gas equipment |
| Electrical insulation condition | Transformer, electrical panels, signal device etc |
| Corrosion resist condition | Absorption tower, chemical pipe, water treatment equipment, desulfurization tower etc |
| Non-magnetic condition | Computer parts, robot parts, fuel battery etc |
| Light weight condition | Auto parts, aerospace parts, ship parts etc |
| Technical parameter: | |||
| No. | Technical specification | Unit | Specification value |
| 1 | Density(at 20ºC±2ºC) | g/cm3 | ≥2.2 |
| 2 | Water absorption rate (at 20ºC±2ºC,24h) | % | ≤0.05 |
| 3 | Tensile strength | Mpa | ≥1200 |
| 4 | Bending strength | Mpa | ≥960 |
| 5 | Dye penetrated test | Min | ≥15 |
| 6 | Water diffusion test (1%NaCl,Boiling for 100h 12kv/1min) | mA | ≤0.1 |
| 7 | Shearing strength along laminas | Mpa | ≥50 |
| 8 | Volume resistivity (140ºC,96h) | Ω.M | ≥1010 |
| 9 | DC withstand voltage (10mm) | Kv | ≥50 |
| 10 | Lighting surge withstand voltage (100kv,10mm) | Times | ≥5 |
| 11 | Bending strength at heating conditions | Mpa/150ºC | ≥350 |
| 12 | Torsion strength | Mpa | ≥800 |
Our product is made of fiberglass and epoxy resin mixed continuous pultrusion, which makes the product resistance to mechanical stress and mechanical tension are very good, the tensile strength of 1500MPa, far more than 45 steel casting tensile strength 570Mpa indicators. Electrical performance, voltage level for the 10kV - 1000kV voltage range. Corrosion resistance, high bending strength, not easy to bend, easy to use and so on.
Products allow long-term working temperature of 170-210 ºC , product maximum short-circuit working temperature of 260 ºC (time is less than 5 seconds).
Products choose Germany release agent, so as to ensure that the surface of the product is very smooth without color difference, no glitches, no scratches.
The heat-resistant grade and the insulation grade of the product all reach H grade.
In addition to the above products, we also provide the following products.
- Epoxy glass cloth laminated sheets
EPGC201,EPGC202 board are from electrical alkali-free glass cloth with epoxy resin Baptist,formed by hot pressing,Products with high mechanical properties and electrical performance.
EPGC201 epoxy glass cloth laminate applied to B-class motors.electrical equipment for insulation of structural parts.
EPGC202 epoxy glass cloth laminated sheets have flame-retardant requirements applicable to the B-class motors.electrical equipment for insulation of structural parts as other Purposes.
Product Description
EPGC203,EPGC204 plates are from 7628 glass cloth with epoxy resin Baptist,formed by hot pressing.Products with high mechanical properties.
EPGC203 epoxy glass cloth laminate applied to F-class motors,electrical equipment for insulation of structural parts.
EPGC204 epoxy glass cloth laminated sheets have flame-retardant requirements applicable to the F-class motors,electrical equipment for insulation of structural parts.
Technical parameters
| No | Item | Units | Indicators | ||||
| EPGC201 | EPGC202 | EPGC203 | EPGC204 | ||||
| 1 | Density | g/sqcm | 1.7-1.9 | 1.7-1.9 | 1.8-2.0 | 1.8-2.0 | |
| 2 | Vertical layer to the bending strength | Vertical | Mpa | 340 | 340 | 340 | 340 |
| Horizontal | 250 | 250 | 170 | 170 | |||
| 3 | Impact strength (simply supported beam method,notched specimen) | KJ/sqm | 37 | 37 | 34 | 34 | |
| 4 | Vertical Flammability | Grade | - | FV-0 | - | FV-0 | |
| 5 | Adhesive strength | N | 6500 | 6500 | - | - | |
| 6 | Insulation Resistance | Normal | Ω | ||||
| Water after 24h | |||||||
| 7 | Parallel to the layer high voltage((90ºC+2ºC oil)) | KV | 35 | 35 | 5 | 5 | |
| 8 | Vertical layers to the electrical strength(90ºC+2ºC oil) | 0.5-1mm | MV/m | 0 | 20 | 20 | 20 |
| 1.1-2mm | 18 | 18 | 18 | 18 | |||
| 2.1-3mm | 16 | 16 | 16 | 16 | |||
- Glass fiber winding tube
Technical parameters
| No. | Item | Units | Indicators | ||
| 1 | Density | g/SQCM | 1.7-1.9 | ||
| 2 | Flexural strength | Normal | Mpa | 340 | |
| 280±2ºC | 150 | ||||
| 3 | Martin Heat(vertical) | ºC | 130 | ||
| 4 | Impact strength | Layer parallel to the notched specimen | KJ/sqm | 33 | |
| Vertical layers to the notched specimen | 150 | ||||
| 5 | Vertical layers to the electrical strength (90ºC+2ºC oil) | MV/m | 18 | ||
| 6 | Insulation Resistance | Normal | Ω | ||
| Water after 24h | |||||
| 7 | Paralle to the layer high voltage (90ºC+2ºC oil) | KV | 30 | ||
| 8 | Frequency dielectric constant | - | 5.5 | ||
| 9 | Frequency dielectric loss factor | - | 0.04 | ||
| 10 | Absorbent | % | 0.05 | ||
- Composite insulating bolt
Technical parameters
| No. | Item | Units | Indicators |
| 1 | Density | g/sqcm | 2.1 |
| 2 | Tensile strength | Mpa | 1200 |
| 3 | Siphon test | Min | 15 |
| 4 | Water diffusion test | MA | 0.5 |
| 5 | Stress corrosion resistance | h | 96 |
| 6 | Bending strength | Mpa | 230 |
| 7 | Volume resistivity | Ω.m | 10 |
| 8 | Fiber content | % | 80 |
| 9 | Power frequency voltage | KV | 50 |
| 10 | Full wave impulse voltage | KV | 100 |
| 11 | Water absorption rate | % | 0.05 |
| 12 | Flame retardant | - | V0 |
- Polymer Composite insulated rod
Polymer composite insulation rod
Using glass fiber impregnated in epoxy resin matrix pultrusion and after high temperature,The product has:light weight,machinery stable performance,excellent insulation performance,can override the 10KV-1000KV voltage range,Tensile properties of products is highlighted particularly,the tensile strength is 1360Mpa or above,significantly more than 45casting steel tensile strength 570Mpa index.Composite insulator composite dielectric properties provides reliable basis,The company production of the mandrel are:General mandrel,high temperature,acid,high temperature resistant mandrel mandrel acid-resistant core bar of four major series of products.
Technical parameters
| No. | Item | Units | Common type | Acid resistant |
| 1 | Density(20ºC±2ºC) | g/sqcm | 2.1 | 2.1 |
| 2 | Water absorption rate(23ºC±1ºC,24h) | % | 0.05 | 0.05 |
| 3 | Tensile strength | Mpa | 1200 | 1200 |
| 4 | Siphon test | Min | 15 | 15 |
| 5 | Water diffusion test | MA | 0.5 | |
| 6 | Volume resistivity(140ºC.96h) | Ω.m | ||
| 7 | Stress corrosion resistance | h | - | 96 |
| 8 | DC breakdown voltage | KV | 50 | 50 |
| 9 | Lightning impulse voltage(100KV) | Times | 5 | 5 |
| 10 | Hot bending failure load test(143ºC+1ºC) | % | 230 | 230 |
| 11 | Flame retardant | - | V0 | V0 |
- Ultra high voltage insulation pull rod
Instruction:Dipped and stove to prep reg by electronic grade glass fiber cloth,epoxy,pyruvate,dicyandiamide.DMF and a small amount of chemical materials.
Character,
1.Glossy and smooth service.uniform thickness and without other impurities,
2.The specification and colors can be produced according to customers' requirement.
3.Time of g elation and percent of gel can controlled according to customers' requirement,
Width,1270mm,1260mm,1250mm,1100mm.
Thickness,7628/190g~20g 1506/150g~160g 2116/110g~130g
Color:pale green,pale yellow,anti-static and black.
Usage,Used to PCB CCL and various of isolation plates.
The company has processing center and advanced equipment.according to customer's pictures,drawings of samples of the design,production,processing services,for customers to find the best solution for the application of ,Products are mainly used in large motor,switch cabinets,electrical control cabinet, inverters,transformers and other fields.
Two benzene ether laminate,Have excellent mechanical properties,electrical properties and chemical corrosion resistance and radiation resistance,Applicable to H machinery,parts for electrical insulation in the results.
Melamine board.With high mechanical properties,electrical properties,and excellent flame retardancy and arc resistance,Suitable for electrical equipment for arc resistant insulation structural parts
Phenolic cotton cloth laminated rod:Has a certain mechanical,electrical properties,but in the use of transformer oil.used in electrical appliance insulation structural parts.
Laminate standard thickness:0.3mm-80mm
Laminate standard standard diameter:6mm-200mm
Remarks:Customer's special requirement on specifications could be negotiated by buyer and seller case by case
Glass Cloth Laminates Type:3240 series 3240,3240-1,3240-3,EPGC series EPGC 201,EPGC202,EPGC203,EPGC204,EPGC205,EPGC306,EPGC307,EPGC308;FR-4,FR-5,G-11,etc
Characteristics&Applications:With high mechanical strength,electrical properties and ,good moisture resistance properties,widely range of applications,for example:suitable for using as insulation structural parts in electric equipment,such as electric generators,motors,etc.
Phenolic Cotton Cloth Laminates Type:3025,3026,3027,3028;PFCC series PFCC201,PFCC202,PFCC203,FPCC204;C850 series C850.1,C850.2(CE),C850.3,C850.4(LE),etc
Characteristic&Applications:Widely range of applications in mechanical and electrical field,for example:suitable for using as insulation structural parts of machinery and electric equipment.such as electric generators,motors,switch board,e
Phenolic Paper Laminates Type:3020,3021 series 3021,302B,3021C,3021D;PFCP series of PFCP201,PFCP202,PFCP203,PFCP206,PFCP207,PFCP308,etc.
Characteristics&Applications:Widely range of applications,for examples,suitable for using as insulation structural parts of machinery and electric equipment,such as electric generators,motors,switch board,etc.
Molded Rod Type:phenolic cotton cloth rod 3721,3722,3723,3724,3725;epoxy glass cloth 3840,3841,etc.
Characteristics&Applications:Used in mechanical and electrical.
FAQ
1. Where are you located?
We are located in TIANJIN city, China, near to Beijing.
2. Do you accept small / sample order? And lead time?
Sample are available, lead time according factory production plan, uauslly 7-25 days.
3. How do you ship the goods?
We ship the goods by Sea, or by express, specific discussion.
4. Do you accept OEM or ODM order?
Yes, OEM and ODM order are welcome.
5. What payment do you accept?
L/C at sight, T/T, Western Union, etc.
Packaging & Delivery
Packaging Details
suitable packing for export. PP bag, Carton box, Pallet/ Or according customer requirement.
1.Inside packing: a plastic bag or woven belt
2.Outside packing: carton box and pallet.
3.According customer requirement.
Delivery Time: 3~7days
Please Contact Us
Miss: lydia
Mob: 86-13752439076 Fax: 86-22-60863016
http://chinainsulation.en.made-in-china.com